KD8008M is a Kapton Tape Adhesive featuring two sides coated silicone adhesive that offers high temperature resistance as well as reduced static discharge properties.
Low Electrostatic Discharge at Unwind
Excellent Tensile Strength and Elongation Resistant up to 500 F Both-Face Adhesion without residue after Removal.
Masking printed circuit boards during wave solder or solder dip process. Protecting contacts during spray painting, powder coating & solder
coating processes.
Bundling transformers, motors batteries & electronic components together for insulation purposes.
| Item | Typical Value | Test Method | ||
| Imperial | Metric | |||
| Backing | 3.32mil | 0.083±0.00m | / | |
| Total Thickness | 8.2mil | 0.205±0.01mm | / | |
| Adhesion to Steel | A adhesive | >0.62lbs/in | >6.5N/25mm | GB/T 2792-2014 |
| B adhesive | <0.096lbs/in | <1N/25mm | ||
| Surface Resistance | / | <1011ohms | / | |
| Tensile Strength | ≥45.7lbs/in | ≥8 (KN/M) | GB/T 30776-2014 | |
| Elongation | ≥50% | ≥50% | ||
| Static Discharge (Removal from roll) | <200V | <200V | / | |
| Maximum Operating Temperature | 500℉ | 260℃ | / | |
Store at 10-30 and 40-70% relative humidity conditions out of direct sunlight to preserve its shelf life: 12 months from date of manufacturing when stored initially as instructed.
Surface should be clean, dry, free from dust or oil contamination and provide sufficient contact pressure with roller, hand or press when applying adhesive tapes and films to avoid repeat sticking to avoid adhesion decrease.
Please be aware that the data herein has been produced based on laboratory testing and experience only and therefore customer must conduct their own evaluation to ascertain that product meets intended application needs before authorising its use in their intended application.